Perfect matt aluminium spray
ALUSPR-PERFECT-400ML
Register now and access more than 125,000 products
High layer thickness with first spray coat
- Very safe due to optimal protection against the elements
- Minimal time required, as only one work step is necessary
- Provides good coverage
Versatile use thanks to adjustable spray head
Large-area and minor repairs can be carried out quickly and safely with the adjustable spray head.
High degree of resistance to running
High abrasion resistance
Spot weldable
Not suitable as a primer for PU, MS polymer or hybrid sealing compounds.
The usage instructions are recommendations based on the tests we have conducted and our experience. Carry out your own tests before each application. Due to the large number of applications as well as storage and usage conditions, we do not assume any liability for a specific application result. Any technical information or advice provided by our free customer service shall be provided to the exclusion of any liability, unless the advice or information is part of our contractually agreed scope of services or the advisor was acting wilfully. We ensure the consistent quality of our products. We reserve the right to make technical changes and further developments to our products.
Datasheets(X)
Suitable for metal and plastic rims, attractive protection for metal parts, steel constructions, air-conditioning and ventilation technology, truck/trailer parts, motorcycles etc. For visual enhancement, repair and protection against corrosion of metallic surfaces.
The base material must be clean, dry and free from grease. Remove rust and old loose paint, sand and clean. Vigorously shake the can for approx. 2 minutes before use.
Chemical basis | Acrylated alkyd combination |
Contents | 400 ml |
Colour | Aluminium coloured |
Weight of content | 410 g |
Curing time | 8 h |
Dry layer thickness (first back-and-forth motion) | 50 µm |
Fully hardening/curing conditions | At recommended dry layer thickness |
Density | 1.15 g/cm³ |
Min./max. dust-drying time | 20-30 min |
Min. dust-drying time | 20 min |
Max. dust-drying time | 30 min |
Conditions for dust-drying time | at recommended dry layer thickness |
Min./max. grip strength | 45 min-60 min |
Min. grip strength | 45 min |
Max. grip strength | 60 min |
Grip strength conditions | at recommended dry layer thickness |
Max. temperature resistance | 250 °C |
Shelf life from production | 24 Month |
Conditions to maintain shelf life from production | at 10°C to 25°C |
Min. flashing point | -97 °C |
Recoatable/Can be painted over | Conditional, preliminary testing required |
Cross-cut test | MAN 0-1 |
Cross-cut test conditions | in accordance with DIN 53151 |
Spot weldable | No |
AOX-free | Yes |
Substrates with good adhesion | Wood, Metal, Cardboard, PMMA, Polycarbonate, Polystyrene |
Last viewed
1/2-inch impact socket wrench insert hexagon, metric, long
CUTTING DISC FOR STEEL
Pre-charged NiMH battery
Multigrade compressor oil Pro
PU COMPRESSED-AIR HOSE
Twist drill bits HSS DIN 338 type RN TIN head
Shelf for cartridges
Cut and Cool Perfect drilling/cutting paste
Hand cleaner in tube
Cordless angle grinder AWS 18-125 P COMPACT M-CUBE